The LiFePO₄/FePO₄ phase transition process is remarkable in terms of its excellent reversibility, making this redox system extremely promising for high rate lithium storage. The recent observation of ordering effects (Li_0.5FePO₄) during the phase transition challenges the traditional two phase models. In this work, the phenomenon of staging for LiFePO₄ for different sizes (70 nm and 50 nm) by high resolution aberration corrected annular bright electron microscopy is detected, investigated, and discussed along with previous results on larger crystals. In the small crystals, staging is found throughout with a decrease of order from center to the surface. For the larger crystal, a staging phase occurs constituting the interfacial zone (width around 15 nm) between LiFePO₄ and FePO₄. A comparison is made to recent experiments on even larger crystals showing such an interphase of smaller extent (around 2 nm). Thus it appears that these zones narrow with increasing size. These findings are discussed in the light of phase transition thermodynamics and kinetics. In particular, the possibility is discussed that the staging interphase may constitute a low energy solution to the LiFePO₄/FePO₄ contact.

The phenomenon of Li-ordering in the system LiFePO₄/FePO₄ is investigated by STEM-ABF for different sizes. While in small crystals, the ordering affect the whole particle; for larger crystals, it was found to characterize the LiFePO₄/FePO₄ contact and the interfacial zones narrow with increasing size. These findings are discussed in the light of phase transition thermodynamics and kinetics.